- 摻釹釩酸釓晶體(Nd:GdVO4)
摻釹釩酸釓晶體(Nd:GdVO4)
摻釹釩酸釓晶體(Nd:GdVO4)是和摻釹釩酸釔單晶(Nd:YVO4)性質(zhì)相近的優(yōu)秀的激光晶體,具有優(yōu)良的物理、光學、機械性能,是理想的激光二極管泵浦全固態(tài)(DPSS)微小型激光器的激光工作物質(zhì)之一.它比Nd:YAG有更高的斜率效率，比釩酸釔有更好的熱導和高輸出功率，故在高功率DPSS場合，使用Nd:GdVO4的效果會比使用Nd:YAG和Nd:YVO4更好。
Capabilities:
|
Nd dopant:
|
0.2 ~ 3 atm%
|
|
Width x Height:
|
1x1 ~ 16x16mm
|
|
Length:
|
0.02 ~ 20mm
|
Specifications:
|
Orientation:
|
a-cut( ± 0.55° )
|
|
Dimensional Tolerance:
|
+/-0.1mm
|
|
Wavefront Distortion:
|
<λ/8 at 632.8nm
|
|
Surface Quality:
|
20/10
|
|
Parallelism:
|
< 10 arc seconds
|
|
Perpendicularity:
|
< 5 arc minutes
|
|
Surface Flatness:
|
<λ/10 at 632.8nm
|
|
Clear Aperture:
|
Central 95%
|
|
Chamfer:
|
0.15x45°
|
|
Coating:
|
1.AR@1064nm R<0.1%
2.AR@1064nm R< 0.1% & HT@808nm T>95% 3.HR@1064nm R>99.8% & HR@532nm R>99% & HT@808nm T>95% |
Properties:
|
Crystal Structure
|
Zircon Tetragonal, space group D4h, a=b=7.21, c=6.35
|
|
Melting Point
|
1780°C
|
|
Density
|
5.47g/cm3
|
|
Mohs Hardness
|
Glass-like, ~ 5
|
|
Thermal Expansion Coefficient
|
aa=1.5x10-6/K, ac=7.3x10-6/K
|
|
Thermal Conductivity Coefficient
|
11.7 W/m/K <110>
|
|
Peak Absorption Wavelength
|
808.5 nm
|
|
Lasing Wavelength
|
912.6 nm, 1063.1 nm, 1341.3 nm
|
|
Crystal Class
|
positive uniaxial, no=na=nb ne=nc
no=1.9854, ne=2.1981, @ 1064nm no=2.038184, ne=2.292962, @ 532nm no=1.9977322, ne=2.219864, @ 808nm |
|
Thermal Optical Coefficient
|
dn/dT=4.7x10-6/K
|
|
Stimulated Emission Cross-Section
|
7.60x10-19cm2 , @1064 nm
|
|
Fluorescent Lifetime
|
95 ms (1 atm% nd doped) @ 808 nm
|
|
Loss Coefficient
|
0.003 cm-1@ 1064 nm
|
|
Absorption Coefficient
|
74 cm-1 @ 808 nm (1.2%)
|
|
Absorption Length
|
0.32 mm @ 808 nm
|
|
Intrinsic Loss
|
Less 0.1% cm-1 , @1064 nm
|
|
Linewidth
|
0.6 nm
|
|
Polarized Laser Emission
|
parallel to optic axis (c-axis)
|
|
Diode Pumped Optical to Optica
Efficiency |
> 60%
|
Sellmeier Equation (for pure GdVO4 crystals)
ne2=4.734369+0.1216149/(l2 - 0.0523664) - 0.013927l2
no2=3.8987165+0.05990622/(l2 - 0.0514395) - 0.011319l2
Note: Kinds of sizes, coating are available upon request.